Lucky Enpla LHLD1050
| Category: | PC , Polycarbonate |
| Manufacturer: | Lucky Enpla Co LTD |
| Trademark: | Lucky Enpla |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fVqrsM_Lucky-Enpla-LHLD1050.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lucky Enpla LHLD1050 is a polycarbonate (PC) product,. It can be processed by extrusion or injection molding and is available in North America, Europe or Asia Pacific. Typical application areas are: movies. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 - 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 57.9 | MPa | ASTM D638 |
| Flexural Modulus 2 | 2060 | MPa | ASTM D790 |
| Flexural Strength 3 | 83.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (3.18 mm) | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 127 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 90.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 270 - 280 | °C | |
| Middle Temperature | 275 - 290 | °C | |
| Front Temperature | 280 - 290 | °C | |
| Nozzle Temperature | 280 - 300 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Back Pressure | 1.96 - 3.92 | MPa | |
| Screw Speed | 60 - 80 | rpm |
| Injection instructions |
|---|
| Resin Temperature: 280-300°CInjection Pressure (1st Pressure): 700-1200 kg/cm²Injection Pressure (2nd Pressure): 400-800 kg/cm² |
| Note Message | |
|---|---|
| 1 . | 10 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REVOLVE® M-772 | Matrix Polymers | PE, Unspecified | REVOLVE® |
| WPP PP PPC7TF1.3-Natural | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| Hipolyene 6251 Y | Zylog Plastalloys | TPO (POE) | Hipolyene |
| LNP™ LUBRICOMP™ DFL36HL compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ LUBRICOMP™ |
| LNP™ THERMOCOMP™ UF00BAS compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |