LIM™ 6010
| Category: | Silicone Rubber, LSR , Silicone Rubber, LSR |
| Manufacturer: | Momentive Performance Materials Inc. |
| Trademark: | LIM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fVooFO_LIM-6010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LIM6010 liquid silicone rubber is a two-component product formulated for use in liquid injection molding to produce elastomeric parts where low-durometer is a key requirement. LIM6010 elastomer is clear, but easily pigmentable with Momentive masterbatch colors. The combination of low-durometer and non-tackiness allows the product to be used in such consumer goods applications as corn pads and heel inserts, where 'soft touch' sensory characteristics are important. LIM6010 elastomer offers a convenient 1:1 mix ratio and releases easily from molds. Cure time is rapid, generally 10 to 40 seconds at 150°C (302°F) - 204°C (400°F), depending on part size, configuration, and molding temperature. Key Features and Benefits
Potential Applications The combination of low-durometer and non-tackiness allows the product to be used in such consumer goods applications, where 'soft touch' sensory characteristics are important.
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 1.0 | ||
| Part B | Mix Ratio by Weight: 1.0 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | |||
| -- 1 | Clear/Transparent | ||
| -- 2 | Clear/Transparent | ||
| Density | |||
| -- 3 | 1.05 | g/cm³ | |
| -- 4 | 1.05 | g/cm³ | |
| Viscosity | |||
| -- 5 | 30 | Pa·s | |
| -- 6 | 30 | Pa·s |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness | |||
| Shore A 7 | 10 | ||
| Shore A 8 | 15 | ||
| Tensile Modulus | |||
| 100% Secant 9 | 0.250 | MPa | |
| 100% Secant 10 | 0.380 | MPa | |
| Tensile Strength | |||
| -- 11 | 2.76 | MPa | |
| -- 12 | 3.10 | MPa | |
| Tensile Elongation at Break | |||
| -- 13 | 440 | % | |
| -- 14 | 510 | % | |
| Tear Strength | |||
| Die B 15 | 5.62 | kN/m | |
| Die B 16 | 10.5 | kN/m |
| Note Message | |
|---|---|
| 1 . | Part B |
| 2 . | Part A |
| 3 . | Part B |
| 4 . | Part A |
| 5 . | Part B |
| 6 . | Part A |
| 7 . | As Molded 30 sec @ 177°C (350°F) |
| 8 . | Postbaked 1 hr @ 177°C (350°F) |
| 9 . | As Molded 30 sec @ 177°C (350°F) |
| 10 . | Postbaked 1 hr @ 177°C (350°F) |
| 11 . | As Molded 30 sec @ 177°C (350°F) |
| 12 . | Postbaked 1 hr @ 177°C (350°F) |
| 13 . | Postbaked 1 hr @ 177°C (350°F) |
| 14 . | As Molded 30 sec @ 177°C (350°F) |
| 15 . | As Molded 30 sec @ 177°C (350°F) |
| 16 . | Postbaked 1 hr @ 177°C (350°F) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE F04660 (Blown film) | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| Nipol® LX511A | Zeon Corporation | Latex | Nipol® |
| CMET HS-680 | CMET Inc. | Epoxy | CMET |
| ENFLEX V1065A | ENPLAST Americas, a Ravago Group Company | TPV | ENFLEX |
| Kepex® 3500 | Korea Engineering Plastics Co., Ltd | PBT | Kepex® |