POLYLAC® PA-758R
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | CHI MEI CORPORATION |
| Trademark: | POLYLAC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fViWlB_POLYLAC-PA-758R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYLAC® PA-758R is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.08 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 27.3 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 44.8 | MPa | |
| Break | 33.0 | MPa | |
| Tensile Strain (Break) | 60 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2000 | MPa | ISO 178 |
| Flexural Stress 2 | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -- | 14 | kJ/m² | ISO 179 |
| -- | 11 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength | |||
| -- | 51 | kJ/m² | ISO 179 |
| -- | 57 | kJ/m² | ISO 179/2U |
| Notched Izod Impact Strength | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 55 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | ISO 75-2/A | ||
| 1.8 MPa, Unannealed | 77.6 | °C | |
| 1.8 MPa, Annealed | 96.0 | °C | |
| Vicat Softening Temperature | |||
| -- | 102 | °C | ISO 306/A50 |
| -- | 105 | °C | ISO 306/A120 |
| -- | 93.8 | °C | ISO 306/B50 |
| -- | 97.2 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 200 to 220 | °C | |
| Middle Temperature | 220 to 250 | °C | |
| Front Temperature | 220 to 250 | °C | |
| Processing (Melt) Temp | 230 to 240 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Pressure | 4.90 to 7.85 | MPa | |
| Holding Pressure | 1.96 to 4.90 | MPa | |
| Back Pressure | 0.490 to 0.981 | MPa |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUNFROST® KD70QA | Mitsubishi Chemical Performance Polymers, Inc. | PVC Elastomer | SUNFROST® |
| Zytel® HTN 51G35EF BK083 | DuPont Performance Polymers | PPA | Zytel® HTN |
| Elastron® D P.D300.A80.N | Elastron USA, Inc. | SBS | Elastron® D |
| Haysite Plastics HCR-191 | Haysite Reinforced Plastics | Polyester, TS | Haysite Plastics |
| Karina IVORY PVC COMPOUND KAPU 5535/1-Y(***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |