SCHULAMID® 66 GF 50 H
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fVgKiM_SCHULAMID-66-GF-50-H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 50% glass fiber reinforced, heat stabilized Polyamide 66 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.57 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (23°C, 24 hr) | 1.2 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 300 | 220 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 16500 | 13000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 228 | 180 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.3 | 3.3 | % | ISO 527-2/1A/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 12 | -- | kJ/m² | |
| 23°C | 14 | 18 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 70 | -- | kJ/m² | |
| 23°C | 90 | 94 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | > 250 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | > 250 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | > 250 | -- | °C | ISO 306/A50, ISO 306/B50 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | > 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | > 1.0E+10 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 450 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | < 100 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.50 mm | -- | 600 | °C | |
| 3.00 mm | -- | 600 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SynPlast™ DIDA-E | PolyOne Corporation | Di Isodecyl Adipate | SynPlast™ |
| Vydyne® R860 BK02 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| VALOX™ SHF4960 resin | SABIC Innovative Plastics Europe | PBT | VALOX™ |
| Optix® CA-71 | Plaskolite West, Inc. | Acrylic (PMMA) | Optix® |
| Sylvin 7840-70 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |