LNP™ LUBRICOMP™ RFI12 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fVR1ph_LNP-LUBRICOMP-RFI12-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RFI12 is a compound based on Nylon 66 resin containing 10% Glass Fiber, 2% Silicone. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound RFL-4412 Product reorder name: RFI12 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.90 to 2.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.98 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.5 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 5500 | MPa | ASTM D638 |
| -- | 5260 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 114 | MPa | ASTM D638 |
| Yield | 107 | MPa | ISO 527-2/5 |
| Break 3 | 114 | MPa | ASTM D638 |
| Break | 107 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.8 | % | ASTM D638 |
| Yield | 2.7 | % | ISO 527-2/5 |
| Break 5 | 2.8 | % | ASTM D638 |
| Break | 2.6 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 4780 | MPa | ASTM D790 |
| -- 7 | 4440 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 155 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 166 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 165 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.47 | ||
| vs. Itself - Static | 0.44 | ||
| Wear Factor - Washer | 261 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 41 | J/m | ASTM D256 |
| 23°C 10 | 4.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 460 | J/m | ASTM D4812 |
| 23°C 11 | 28 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 5.60 | J | ASTM D3763 |
| -- | 1.30 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 257 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 255 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 241 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 236 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 6042-40A | RTP Company | TPE | RTP |
| Shin-Etsu RTV KE-3493 | Shin-Etsu Silicones of America | Silicone Rubber, RTV-1 | Shin-Etsu RTV |
| TRIREX® Compound 3025G20 | Samyang Corporation | PC | TRIREX® Compound |
| APEX® 89-P377-A | Teknor Apex Company | PVC, Flexible | APEX® |
| Sylvin 8200-80UV Red 6257 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |