Infino WP-1200
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fV25eB_InfinoWP1200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino WP-1200 is a polycarbonate acrylonitrile butadiene styrene (PC ABS) product, which contains a glass fiber reinforced material. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: automotive industry. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.27 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 36 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.15 - 0.45 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.25 - 0.55 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.25 - 0.55 | % | ISO 2577 |
| Traffic : 3.20mm | 0.15 - 0.45 | % | ISO 2577 |
| Ash Content | |||
| -- | 20 | % | ASTM D5630 |
| -- | 20 | % | ISO 3451 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4200 | MPa | ASTM D638 |
| -- | 4300 | MPa | ISO 527-2/5 |
| Tensile Strength | |||
| Yield 2 | 120 | MPa | ASTM D638 |
| Yield | 109 | MPa | ISO 527-2/5 |
| Fracture 3 | 120 | MPa | ASTM D638 |
| Fracture | 109 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 4 | 3.5 | % | ASTM D638 |
| Fracture | 3.9 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- 5 | 6100 | MPa | ASTM D790 |
| -- 6 | 7400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 150 | MPa | ASTM D790 |
| -- 8 | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 9.0 | kJ/m² | ISO 179/1eA |
| 23°C | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 10 | ISO 179/1eU | ||
| -30°C | 58 | kJ/m² | ISO 179/1eU |
| 23°C | 62 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| -30°C, 3.18 mm | 59 | J/m | ASTM D256 |
| -30°C, 6.35 mm | 69 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 69 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 79 | J/m | ASTM D256 |
| -30°C 11 | 7.0 | kJ/m² | ISO 180/1A |
| 23°C 12 | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 138 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 4.00mm | 131 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 128 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 121 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 130 | °C | ISO 306/B50 |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : 40 to 100°C | 3.1E-6 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Horizontal : 40 to 100°C | 6.4E-6 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 90 - 110 | °C | |
| Hot air dryer | 90 - 110 | °C | |
| Drying Time | |||
| -- | 2.0 - 4.0 | hr | |
| Hot air dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 220 - 240 | °C | |
| Middle Temperature | 240 - 250 | °C | |
| Front Temperature | 250 - 270 | °C | |
| Nozzle Temperature | 250 - 290 | °C | |
| Mold Temperature | 60 - 90 | °C | |
| Injection Pressure | 98.1 | MPa | |
| Back Pressure | 0.490 - 2.94 | MPa | |
| Screw Speed | 5 - 200 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| 11 . | Thickness: 4mm |
| 12 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx FP63E33 | The Matrixx Group, Inc. | Nylon 6 | Matrixx |
| SABIC® PPcompound 3240EH | Saudi Basic Industries Corporation (SABIC) | PP Homopolymer | SABIC® PPcompound |
| Weifang Kingdom CPET101 | Weifang Kingdom Plastic Co., Ltd | CPE | Weifang Kingdom |
| Carboprene® 2530 AV NAT | SO.F.TER. SPA | PP Homopolymer | Carboprene® |
| Petrothene® GA501150X01 | LyondellBasell Industries | LLDPE | Petrothene® |