TPSiV™ 4100-70A
| Category: | TPSiV , Thermoplastic Silicone Vulcanizate |
| Manufacturer: | Multibase, A Dow Corning Company |
| Trademark: | TPSiV™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fUyzG6_TPSiV-4100-70A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TPSiV® 4100-70A Thermoplastic Elastomer is a thermoplastic elastomer with superior compression set and mechanical properties with excellent bonding to Polycarbonate, ABS, and similar polar substrates. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/10.0 kg) | 13 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.0 to 3.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A, 15 sec) | 72 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 28.6 | MPa | ISO 178 |
| Flexural Stress | 2.30 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles) | 64.0 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 3.90 | MPa | ISO 37 |
| Tensile Stress (Yield) | 11.4 | MPa | ISO 37 |
| Tensile Elongation (Break) | 690 | % | ISO 37 |
| Tear Strength | 51 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 22 hr | 9.0 | % | |
| 70°C, 22 hr | 43 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.0 to 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 165 to 175 | °C | |
| Middle Temperature | 170 to 180 | °C | |
| Front Temperature | 180 to 195 | °C | |
| Nozzle Temperature | 185 to 200 | °C | |
| Processing (Melt) Temp | 195 | °C | |
| Mold Temperature | 20.0 to 40.0 | °C | |
| Injection Rate | Moderate-Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1483 HEC | RTP Company | PESU | RTP |
| TEKAMID™ TA210G33 | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| Karina IVORY PVC COMPOUND -E 832-35/ 1-Y-ERYB-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Petro Rabigh PP AW564 | Rabigh Refining & Petrochemical Co. | PP Impact Copolymer | Petro Rabigh PP |
| PLUSTEK RA325G4 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |