Zytel® BM70G20HSLX BK537
| Category: | Nylon 66 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fUsTzl_Zytel-BM70G20HSLX-BK537.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% Glass Reinforced, Heat Stabilized, Polyamide 66 Developed for Blow Molding |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.25 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.70 | -- | % | |
| Flow | 0.50 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 6.8 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 2.1 | -- | % | |
| Viscosity Number | 168 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 6500 | 4000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 120 | 77.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.0 | 13 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 3900 | MPa | |
| 1000 hr | -- | 3200 | MPa | |
| Flexural Modulus | 6100 | -- | MPa | ISO 178 |
| Shear Modulus | 1400 | -- | MPa | ISO 6721 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 8.0 | -- | kJ/m² | |
| 23°C | 15 | 16 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 7.5 | 6.0 | kJ/m² | |
| 23°C | 80 | 80 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 8.0 | 6.0 | kJ/m² | |
| 23°C | 14 | 16 | kJ/m² | |
| Unnotched Izod Impact Strength (23°C) | 73 | -- | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 257 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 239 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 60.0 | -- | °C | ISO 11357-2 |
| Melting Temperature 2 | 260 | -- | °C | ISO 11357-3 |
| Fill Analysis | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melt Density | 1.07 | -- | g/cm³ | |
| Melt Viscosity (280°C, 1000 sec^-1) | 330 | -- | Pa·s | ISO 11443 |
| Specific Heat Capacity of Melt | 2000 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.20 | -- | W/m/K |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® Fine Powders T NAT BHV COS | Arkema | Nylon 11 | Rilsan® Fine Powders |
| RTP 201A HI | RTP Company | Nylon 6 | RTP |
| CERTENE™ SGM-140 | Muehlstein | PS (GPPS) | CERTENE™ |
| Delrin® 500SC NC010 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| Jiangsu Sinarise EX8535X | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |