EXCELLOY TK12G20
| Category: | ABS+PBT , Acrylonitrile Butadiene Styrene + PBT |
| Manufacturer: | Techno Polymer Co, Ltd. |
| Trademark: | EXCELLOY |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fUlY8T_EXCELLOY-TK12G20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EXCELLOY TK12G20 is an Acrylonitrile Butadiene Styrene + PBT (ABS+PBT) product filled with 20% glass fiber. It can be processed by injection molding and is available in Asia Pacific or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.28 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (260°C/10.0 kg) | 40 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.20 to 0.50 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 113 | ASTM D785 | |
| R-Scale | 111 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 90.2 | MPa | ASTM D638 |
| Yield | 84.0 | MPa | ISO 527-2 |
| Flexural Modulus | |||
| -- | 5490 | MPa | ASTM D790 |
| -- | 5080 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 134 | MPa | ASTM D790 |
| -- | 138 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 13 | kJ/m² | ISO 179 |
| Notched Izod Impact | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 124 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 130 | °C | ISO 75-2/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (NC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 2.0 to 5.0 | hr | |
| Rear Temperature | 220 to 270 | °C | |
| Middle Temperature | 220 to 270 | °C | |
| Front Temperature | 220 to 270 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RELENE® M60200 | Reliance Industries Limited | HDPE | RELENE® |
| TECAST™ 6XAU | Ensinger Inc. | Nylon 6 | TECAST™ |
| Iupital® F20-03 | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |
| PENTAMID B MK15 H natur | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |
| Sylvin 5175-92 White 1478 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |