Ad-Tech Epoxy EL-324-1
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Ad-Tech Plastic Systems Corp. |
| Trademark: | Ad-Tech Epoxy |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fU0BOX_Ad-Tech-Epoxy-EL-324-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ad-Tech Epoxy EL-324-1 is an Epoxy; Epoxide (Epoxy) product. It can be processed by laminating and is available in North America. Typical application: Coating Applications. Primary characteristic: low shrinkage. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Density | 0.36 | g/cm³ | ASTM D1895 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 30 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 260 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 3.20 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 179 | MPa | ASTM D790 |
| Compressive Strength | 4.45 | MPa | ASTM D695 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 1.0 Mix Ratio by Weight: 100 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 1.0 | ||
| Pot Life (25°C) | 120 to 180 | min | |
| Demold Time (25°C) | 7200 to 10000 | min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BT33 ST | A. Schulman Europe | Nylon 6 | VITAMIDE® |
| LNP™ LUBRICOMP™ ML003S compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ LUBRICOMP™ |
| Pier One PC/ABS C1200 BK | Pier One Polymers, Inc. | PC+ABS | Pier One PC/ABS |
| PENTESTER BT H black | PENTAC Polymer GmbH | PBT | PENTESTER BT |
| ULTEM™ 1000P resin | SABIC Innovative Plastics | PEI | ULTEM™ |