EPLAMID 6 GI0 15 NC
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | EPSAN Plastik SAN. ve TiC. A.S. |
| Trademark: | EPLAMID 6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fT0nXT_EPLAMID-6-GI0-15-NC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Flame retardant polyamide 6 reinforced with 15% of glass fiber, impact modified , heat stabilized for injection moulding. Eplamid 6 GI0 15 is used in all sectors of industry, offering a good impact strength for mechanical properties, with rating UL94 V0 and glow-wire at 960°C. This material is available in natural and in colours on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.36 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 3.00mm | 0.90 | -- | % | ISO 294-4 |
| Flow direction : 3.00mm | 0.60 | -- | % | ISO 294-4 |
| Moisture Content | 0.20 | -- | % | ISO 15512 |
| Ash Content | 15 | -- | % | ISO 3451-4 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 82 | -- | ISO 868 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 5200 | 4900 | MPa | ISO 527-2/50 |
| Tensile Stress (Break, 23°C) | 80.0 | 74.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 5.0 | 10 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 5100 | 5000 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 140 | 120 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 16 | 18 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 15 | 17 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature (DSC) | 215 | -- | °C | ISO 3146 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (3.00 mm) | V-0 | -- | UL 94, IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index (3.00 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (3.00 mm) | 750 | -- | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 干燥 TEST CONDITIONS: Laboratory conditions are 23 ±2°C and 45-55 % RH. |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 280 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx MPP2A25HC | The Matrixx Group, Inc. | PP Copolymer | Matrixx |
| Zhongfa PA66 MC66G25FR | Yuyao Zhongfa Engineering Plastics Co. Ltd. | Nylon 66 | Zhongfa |
| Borealis PP SA233CF | Borealis AG | PP Random Copolymer | Borealis PP |
| DISTRUMID 6 GMF30 HSUV | Distrupol | Nylon 6 | DISTRUMID |
| LNP™ FARADEX™ ES003E compound | SABIC Innovative Plastics | PEI | LNP™ FARADEX™ |