LEXAN™ BFL2015 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fSY5iy_LEXAN-BFL2015-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Non-brominated, non-chlorinated flame retardant, glass reinforced PC. Opaque colors only |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.23 | g/cm³ | ASTM D792 |
| -- | 1.30 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 6.5 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 6.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow 1 | 0.20 to 0.50 | % | |
| Flow : 3.20 mm | 0.20 to 0.50 | % | |
| Across Flow : 3.20 mm | 0.20 to 0.50 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.35 | % | |
| Equilibrium, 23°C, 50% RH | 0.15 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 5330 | MPa | ASTM D638 |
| -- | 4960 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 92.0 | MPa | ASTM D638 |
| Yield | 103 | MPa | ISO 527-2/50 |
| Break 4 | 91.0 | MPa | ASTM D638 |
| Break | 101 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 5 | 3.5 | % | ASTM D638 |
| Yield | 3.7 | % | ISO 527-2/50 |
| Break 6 | 4.0 | % | ASTM D638 |
| Break | 4.4 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 7 | 4600 | MPa | ASTM D790 |
| -- 8 | 4290 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 150 | MPa | ISO 178 |
| Yield, 50.0 mm Span 9 | 156 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C 10 | 6.0 | kJ/m² | ISO 179/1eA |
| -30°C | 9.0 | kJ/m² | ISO 179/2C |
| 23°C 11 | 8.0 | kJ/m² | ISO 179/1eA |
| 23°C | 12 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength | |||
| -30°C 12 | 100 | kJ/m² | ISO 179/1eU |
| -30°C | 76 | kJ/m² | ISO 179/2U |
| 23°C 13 | 100 | kJ/m² | ISO 179/1eU |
| 23°C | 68 | kJ/m² | ISO 179/2U |
| Notched Izod Impact | |||
| 23°C | 78 | J/m | ASTM D256 |
| -30°C 14 | 7.0 | kJ/m² | ISO 180/1A |
| 23°C 15 | 8.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 16 | ISO 180/1U | ||
| -30°C | 80 | kJ/m² | |
| 23°C | 80 | kJ/m² | |
| Instrumented Dart Impact (23°C, Total Energy) | 61.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 145 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 141 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 17 | 132 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 148 | °C | ASTM D1525 18 |
| -- | 150 | °C | ISO 306/B50 |
| -- | 151 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | |||
| Flow : -30 to 30°C | 4.0E-5 | cm/cm/°C | ASTM D696 |
| Flow : 23 to 80°C | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -30 to 30°C | 4.0E-5 | cm/cm/°C | ASTM D696 |
| Transverse : 23 to 80°C | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI Str | 80.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (1.60 mm, in Oil) | 20 | kV/mm | ASTM D149 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 3.20 | ||
| 60 Hz | 3.20 | ||
| 1 MHz | 3.10 | ||
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 0.020 | ||
| 60 Hz | 0.020 | ||
| 1 MHz | 0.010 | ||
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 825 | °C | IEC 60695-2-13 |
| Oxygen Index | 38 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 270 to 300 | °C | |
| Middle Temperature | 280 to 310 | °C | |
| Front Temperature | 290 to 320 | °C | |
| Nozzle Temperature | 280 to 310 | °C | |
| Processing (Melt) Temp | 290 to 320 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 5.0 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | Type I, 50 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*3 sp=62mm |
| 11 . | 80*10*3 sp=62mm |
| 12 . | 80*10*3 sp=62mm |
| 13 . | 80*10*3 sp=62mm |
| 14 . | 80*10*3 |
| 15 . | 80*10*3 |
| 16 . | 80*10*3 |
| 17 . | 80*10*4 mm |
| 18 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMTOUGH PZ740 | Polyram Ram-On Industries | PC | RAMTOUGH |
| TOLEN H452 IM | SIBUR, LLC | PP Homopolymer | TOLEN |
| Axiall PVC 12770 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Grilon® TSM-30/2 | EMS-GRIVORY | Nylon 66/6 | Grilon® |
| Formolon® AWS | Formosa Plastics Corporation, U.S.A. | PVC, Unspecified | Formolon® |