Tufpet PBT G2430
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Mitsubishi Rayon America Inc. |
| Trademark: | Tufpet |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fSFtpM_Tufpet-PBT-G2430.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tufpet PBT G2430 is a Polybutylene Terephthalate (PBT) material filled with 30% glass fiber. It is available in North America for injection molding. Important attributes of Tufpet PBT G2430 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.72 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 108 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.5 | % | ASTM D638 |
| Flexural Modulus | 10800 | MPa | ASTM D790 |
| Flexural Strength | 186 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 78 | J/m | ASTM D256 |
| Unnotched Izod Impact | 440 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 220 | °C | |
| 1.8 MPa, Unannealed | 210 | °C | |
| RTI Elec | UL 746 | ||
| 0.790 mm | 130 | °C | |
| 1.57 mm | 130 | °C | |
| 3.18 mm | 130 | °C | |
| RTI Imp | UL 746 | ||
| 0.790 mm | 120 | °C | |
| 1.57 mm | 120 | °C | |
| 3.18 mm | 125 | °C | |
| RTI Str | UL 746 | ||
| 0.790 mm | 120 | °C | |
| 1.57 mm | 120 | °C | |
| 3.18 mm | 130 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 3.0E+18 | ohms·cm | ASTM D257 |
| Dielectric Strength | 21 | kV/mm | ASTM D149 |
| Arc Resistance | 125 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 240 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.790 mm | V-0 | ||
| 1.57 mm | V-0 | ||
| 3.18 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 230 to 303 | °C | |
| Middle Temperature | 230 to 303 | °C | |
| Front Temperature | 230 to 303 | °C | |
| Mold Temperature | 40.0 to 100 | °C | |
| Injection Pressure | 81.4 | MPa | |
| Screw Speed | 80 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Hanwha Total PP RJ700 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Hostacom EKC 265N | LyondellBasell Industries | PP, Unspecified | Hostacom |
| LNP™ STAT-KON™ DD0009XP compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ STAT-KON™ |
| SHINSTRA AG20TKB (PA66) | Shinil Chemical Industry Co., Ltd. | Nylon 66 | SHINSTRA |
| LNP™ THERMOCOMP™ UC008H compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |