RheTech Thermoplastic Polyolefin FT4200-00
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | RheTech, Inc. |
| Trademark: | RheTech Thermoplastic Polyolefin |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fR2tZw_RheTech-Thermoplastic-Polyolefin-FT4200-00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermoplastic Polyolefin, 150K Flexural Modulus, Non-UV Stabilized, Natural. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 61 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 15.9 | MPa | ASTM D638 |
| Flexural Modulus | 1030 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 160 | J/m | ASTM D256 |
| Dart Drop Impact | 13.6 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 73.9 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 48.9 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 - 82.2 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 204 - 232 | °C | |
| Middle Temperature | 210 - 238 | °C | |
| Front Temperature | 216 - 243 | °C | |
| Nozzle Temperature | 221 - 232 | °C | |
| Mold Temperature | 26.7 - 48.9 | °C | |
| Injection Pressure | 2.76 - 10.3 | MPa | |
| Holding Pressure | 2.07 - 8.27 | MPa | |
| Back Pressure | 0.345 - 1.03 | MPa |
| Injection instructions |
|---|
| Injection Speed: Variable -- Application DependantScrew RPM: Recovery 3 seconds before mold opensCycle Time: Wall Thickness Dependant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC VDM80E | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| TRANSMARE® 35HNF50-0.001 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| GERMAMID 6.6 GF 10 | Kunststoff-Kontor-Hamburg GmbH | Nylon 66 | GERMAMID |
| Latamid 66 H2 K/30 | LATI S.p.A. | Nylon 66 | Latamid |
| K-Bin Rigid PVC KBD-5001 | K-Bin, Inc. | PVC, Unspecified | K-Bin Rigid PVC |