Braskem PE LL5400S
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fQk4El_BraskemPELL5400S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LL5400S is a Linear Low Density Polyethylene developed for blown film extrusion in blends with polyethylenes. Films obtained with this product show a good processing performance balanced with good optical and mechanical properties as well as sealability. Very low gel amount. It contains antioxidant additives. Applications: Liners; LDPE and HDPE blends and packages for general use. Others applications: blends for irrigation pipes. Process: Recommended processing conditions for film extrusion about 170 - 210 °C. The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 38 µm, blown film | 40.0 | MPa | ASTM D882 |
| TD : Broken, 38 µm, blown film | 30.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 38 µm, blown film | 1100 | % | ASTM D882 |
| TD : Broken, 38 µm, blown film | 1400 | % | ASTM D882 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant, MD : 38 µm, Blown Film | 170 | MPa | ASTM D790 |
| 1% Secant, TD : 38 µm, Blown Film | 200 | MPa | ASTM D790 |
| Dart Drop Impact (38 µm, Blown Film) | 120 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, blown film | 100 | g | ASTM D1922 |
| TD : 38 µm, blown film | 400 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 38.0 µm, Blown Film) | 110 | ASTM D2457 | |
| Haze (38.0 µm, Blown Film) | 10 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds HM-269H-1000 | Ravago Manufacturing Americas, LLC | PE, Unspecified | Ravago Compounds |
| XYLEX™ X8303CL resin | SABIC Innovative Plastics Europe | PC+Polyester | XYLEX™ |
| Kingfa MAC-601 | Kingfa | PC+ABS | Kingfa |
| Plaslube® J-1/30/TF/13/SI/2 NAT | Techmer Engineered Solutions | Nylon 66 | Plaslube® |
| ESTOPLAST EP 5010BB29 | Ester Industries Ltd. | PBT | ESTOPLAST EP |