EXCELLOY AK10
| Category: | ABS+Nylon , Acrylonitrile Butadiene Styrene + Nylon |
| Manufacturer: | Techno Polymer Co, Ltd. |
| Trademark: | EXCELLOY |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fQEgn7_EXCELLOY-AK10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EXCELLOY AK10 is an Acrylonitrile Butadiene Styrene + Nylon (ABS+Nylon) product. It can be processed by injection molding and is available in Asia Pacific or North America. Primary characteristic: chemical resistant. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.05 | -- | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (260°C/10.0 kg) | 35 | -- | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.70 | -- | % | ISO 294-4 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ||||
| R-Scale | 110 | 101 | ASTM D785 | |
| R-Scale | 109 | 100 | ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | ||||
| Yield | 52.0 | 40.2 | MPa | ASTM D638 |
| Yield | 50.0 | 39.0 | MPa | ISO 527-2 |
| Flexural Modulus | ||||
| -- | 2500 | 1960 | MPa | ASTM D790 |
| -- | 2090 | 1610 | MPa | ISO 178 |
| Flexural Strength | ||||
| -- | 84.3 | 63.7 | MPa | ASTM D790 |
| -- | 75.0 | 55.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 11 | 24 | kJ/m² | ISO 179 |
| Notched Izod Impact | 120 | 250 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 92.0 | 85.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 78.0 | 72.0 | °C | ISO 75-2/B |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 2.0 to 5.0 | hr | |
| Rear Temperature | 240 to 280 | °C | |
| Middle Temperature | 240 to 280 | °C | |
| Front Temperature | 240 to 280 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROLOX 10 G4 DX03 | Taro Plast S.p.A. | PBT | TAROLOX |
| NEFTEKHIM PP 1425J (T28C) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| Nanjing Hongrui PA6 B1302 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 6 | Nanjing Hongrui PA6 |
| LNP™ THERMOCOMP™ RF006L compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Celanex® 1600USFDA | Celanese Corporation | PBT | Celanex® |