STYRON A-TECH™ 1200
| Category: | PS (HIPS) , Polystyrene Resin |
| Manufacturer: | Trinseo |
| Trademark: | STYRON A-TECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fPm6XV_STYRON-A-TECH-1200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
STYRON A-TECH™ 1200 is a newly developed, high-impact polystyrene (HIPS) resin based on patented technology. The technology platform for STYRON A-Tech makes it possible to eliminate the typical trade-offs among the key properties for HIPS including toughness, gloss, stiffness and processability. Main Characteristics:
Applications:
Complies with:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | |||
| -- | 1.05 | g/cm³ | ISO 1183 |
| -- | 1050 | kg/m³ | ISO 1183 1 |
| Apparent Density | 0.60 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 5.0 | g/10 min | ISO 1133 |
| Melt volume-flow rate (200°C/5.0 kg) | 5.00 | cm³/10min | ISO 1133 2 |
| Water Absorption | ISO 62 3 | ||
| Saturation | 0.0 | % | |
| Equilibrium | 0.10 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1750 | MPa | ISO 527-2/1, ISO 527-2 3 4 |
| Tensile Stress | |||
| Yield | 19.5 | MPa | ISO 527-2/5 |
| Yield | 19.0 | MPa | ISO 527-2 5 |
| Break | 22.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Yield) | 1.3 | % | ISO 527-2 6 |
| Nominal Tensile Strain at Break | |||
| -- | 65 | % | ISO 527-2/5 |
| -- | > 50 | % | ISO 527-2 7 |
| Flexural Modulus | 1950 | MPa | ISO 178 |
| Flexural Stress | 38.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy notched impact strength | ISO 179/1eA 8 | ||
| -30°C | 8.00 | kJ/m² | |
| 23°C | 12.0 | kJ/m² | |
| Charpy impact strength | ISO 179/1eU 9 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | 14 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ISO 75-2 10 | ||
| 0.45 MPa | 79.0 | °C | |
| 1.8 MPa | 66.0 | °C | |
| Vicat Softening Temperature | |||
| -- | 100 | °C | ISO 306/A120 |
| 50°C/h, B (50N) | 85.0 | °C | ISO 306 11 |
| CLTE | ISO 11359-2 12 | ||
| Flow | 9.0E-5 | cm/cm/°C | |
| Transverse | 7.0E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6.6 7510 GF 50 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| TEREZ PC 1007 GF 10 | TER HELL PLASTIC GMBH | PC | TEREZ PC |
| Durethan® B 35 F KA 000000 | LANXESS Corporation | Nylon 6 | Durethan® |
| PIVINEL™ PVC MAN150KV | HELLENIC CABLES S.A. | PVC, Unspecified | PIVINEL™ |
| TechnoDur PBT4 GF 30 FR Natural (9975) | TechnoCompound GmbH | PBT | TechnoDur |