Latamid 66 VH2 G/30
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latamid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fPRNEf_Latamid-66-VH2-G-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Compound based on Polyamide 66 (PA 66). Improved thermal stabilisation. Glass fibres. Product UL certified. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.75 to 1.1 | % | |
| Flow : 2.00 mm | 0.35 to 0.65 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 10400 | MPa | |
| 60°C | 6200 | MPa | |
| 90°C | 5000 | MPa | |
| 120°C | 3800 | MPa | |
| 150°C | 3300 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 60°C | 105 | MPa | |
| Yield, 90°C | 85.0 | MPa | |
| Yield, 120°C | 75.0 | MPa | |
| Yield, 150°C | 65.0 | MPa | |
| Break, 23°C | 150 | MPa | |
| Break, 60°C | 100 | MPa | |
| Break, 90°C | 80.0 | MPa | |
| Break, 120°C | 70.0 | MPa | |
| Break, 150°C | 65.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 60°C | 4.0 | % | |
| Yield, 90°C | 5.0 | % | |
| Yield, 120°C | 6.0 | % | |
| Yield, 150°C | 6.0 | % | |
| Break, 23°C | 2.5 | % | |
| Break, 60°C | 4.5 | % | |
| Break, 90°C | 5.0 | % | |
| Break, 120°C | 6.0 | % | |
| Break, 150°C | 6.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 5.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 50 | kJ/m² | |
| 23°C | 55 | kJ/m² | |
| Notched Izod Impact | ASTM D256A | ||
| -20°C, 3.20 mm | 55 | J/m | |
| 23°C, 3.20 mm | 75 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 260 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 240 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 130 | °C | |
| Vicat Softening Temperature | 255 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 8.0E-6 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Oxygen Index | 27 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | > 3.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TUFNYL® RGF 25 HS BLACK | SRF Ltd. | Nylon 66 | TUFNYL® |
| Edistir® RT 441M | Versalis S.p.A. | PS (HIPS) | Edistir® |
| LNP™ COLORCOMP™ J1000AE compound | SABIC Innovative Plastics | PESU | LNP™ COLORCOMP™ |
| Karina BLACK PVC COMPOUND 510D48/ 1-AY | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ Noryl_NWR5810 compound | SABIC Innovative Plastics | PPE+PS | LNP™ LUBRICOMP™ |