TARFLON™ NEO GG1920
| Category: | PC , Polycarbonate |
| Manufacturer: | Idemitsu Kosan Co., Ltd. |
| Trademark: | TARFLON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fPIifd_TARFLON-NEO-GG1920.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GF reinforced, High impact |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 6.00 | cm³/10min | ISO 1133 |
| Spiral Flow | 26.0 | cm | Internal Method |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 2.00 mm | 0.51 | % | |
| Flow : 2.00 mm | 0.38 | % | |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.090 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | ||
| M-Scale | 70 | ||
| R-Scale | 120 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 105 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 5300 | MPa | ISO 178 |
| Flexural Stress | 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 18 | kJ/m² | |
| 0°C | 18 | kJ/m² | |
| 23°C | 22 | kJ/m² | |
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 170 | J/m | |
| 23°C | 190 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 148 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 144 | °C | ISO 75-2/A |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| ISO Shortname | >PC-GF20< |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 5.0 to 8.0 | hr | |
| Rear Temperature | 270 to 310 | °C | |
| Middle Temperature | 270 to 310 | °C | |
| Front Temperature | 270 to 310 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 24h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Witcom POM-C 2A/2L1 | Witcom Engineering Plastics B.V. | Acetal (POM) Copolymer | Witcom POM-C |
| DAI-EL™ G-7801 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |
| ESTOPLAST MG 7030 | Ester Industries Ltd. | PET | ESTOPLAST MG |
| FRIANYL® A3 GF25 V0P2 | Nilit Plastics | Nylon 66 | FRIANYL® |
| Hylon® N7243HL | Ravago Manufacturing Americas, LLC | Nylon 6/12 | Hylon® |