Arnitel® XG5858
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Arnitel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fOt9QE_Arnitel-XG5858.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Arnitel® XG5858 is a Thermoplastic Copolyester Elastomer (TPC-ET) material. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Arnitel® XG5858: Flame Rated. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 13.8 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.16 | % | |
| Equilibrium, 23°C, 50% RH | 0.45 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A, 3 sec) | 82 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 55.0 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Break | 8.80 | MPa | |
| 10% Strain | 1.90 | MPa | |
| 100% Strain | 4.10 | MPa | |
| Nominal Tensile Strain at Break | 550 | % | ISO 527-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature 1 | 180 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 8.4E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 22 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification (0.800 mm) | V-2 | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 150 to 180 | °C | |
| Middle Temperature | 180 to 200 | °C | |
| Front Temperature | 190 to 215 | °C | |
| Nozzle Temperature | 190 to 230 | °C | |
| Processing (Melt) Temp | 190 to 240 | °C | |
| Mold Temperature | 20.0 to 50.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 2.00 to 5.00 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMOFIN PPH300G8 | Polyram Ram-On Industries | PP Homopolymer | RAMOFIN |
| Toyolac® 900 352A | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| Bayfit® 49BM02(80 Index, 92 kg/m³) | Covestro - PUR | PUR, Unspecified | Bayfit® |
| Delrin® 500SC NC010 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| ULTEM™ AUT230 resin | SABIC Innovative Plastics | PEI | ULTEM™ |