TAROLOX 10 G4 DX03 Datasheet,PBT,Taro Plast S.p.A.-SHANGHAI SUSHENG

Message
TAROLOX 10 G4 DX03 is a polybutene terephthalate (PBT) product, which contains a 20% glass fiber reinforced material. It can be processed by injection molding and is available in Europe. Features include: flame retardant/rated flame Good dimensional stability beautiful heat stabilizer mold release agent

General Information
Filler / Reinforcement	Glass fiber reinforced material, 20% filler by weight
Additive	heat stabilizer demoulding
Features	Good dimensional stability Good liquidity Track Resistance Thermal Stability Good demoulding performance Excellent appearance Self-extinguishing
Appearance	Available colors
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.53	g/cm³	ASTM D792, ISO 1183
Molding Shrinkage			ASTM D955
Flow	0.40 - 0.60	%	ASTM D955
Transverse flow	0.60 - 0.90	%	ASTM D955
Water Absorption
23°C, 24 hr	0.050	%	ASTM D570, ISO 62
Saturation	0.25	%	ASTM D570
Saturated, 23°C	0.25	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	118		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	8000	MPa	ASTM D638, ISO 527-2
Tensile Strength (Break)	110	MPa	ASTM D638, ISO 527-2
Tensile Elongation (Break)	3.0	%	ASTM D638, ISO 527-2
Flexural Modulus	7500	MPa	ASTM D790, ISO 178
Flexural Stress
--	165	MPa	ISO 178
Fracture	165	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	5.5	kJ/m²	ISO 179
Notched Izod Impact (23°C, 3.20 mm)	65	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load
0.45 MPa, not annealed	215	°C	ASTM D648, ISO 75-2/B
1.8 MPa, not annealed	205	°C	ASTM D648, ISO 75-2/A
Continuous Use Temperature	75.0	°C	ASTM D794
Vicat Softening Temperature
--	215	°C	ASTM D1525, ISO 306/A50 1 ¹
--	210	°C	ASTM D1525, ISO 306/B50 2 ²
Melting Temperature	220 - 225	°C
CLTE - Flow (-30 to 30°C)	3.0E-5	cm/cm/°C	ASTM D696

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	1.0E+15	ohms·cm	ASTM D257
Dielectric Strength (2.00 mm)	24	kV/mm	ASTM D149
Comparative Tracking Index			IEC 60112
Solution a	250	V	IEC 60112
Solution B	200	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating			UL 94
1.60 mm	V-1		UL 94
3.20 mm	V-0		UL 94
Glow Wire Ignition Temperature (2.00 mm)	960	°C	IEC 60695-2-13
Oxygen Index	31	%	ASTM D2863

Additional Information
Granule Humidity, TARO 002: <0.05%Ball Pressure Test, VDE 0470: 215°CContinuous Service Temperature, UL 94 746B: 75°CContinuous Service Temperature, IEC 216, 130 hr: 90°CContinuous Service Temperature, IEC 216, 160 hr, short term: 130°CDensity, ISO 118: 1.51 to 1.53 Mg/m³Density. ASTM D792: 1.51 to 1.53 Mg/m³Notched Izod Impact Strength , ISO 180, 23°C: 65 J/mCharpy Impact Strength, ASTM D256, 23°C, 4mm: 5.5 kJ/m²Volume Resistivity, ASTM D257: >1e15 ohm-cm

Additional Information

Granule Humidity, TARO 002: <0.05%Ball Pressure Test, VDE 0470: 215°CContinuous Service Temperature, UL 94 746B: 75°CContinuous Service Temperature, IEC 216, 130 hr: 90°CContinuous Service Temperature, IEC 216, 160 hr, short term: 130°CDensity, ISO 118: 1.51 to 1.53 Mg/m³Density. ASTM D792: 1.51 to 1.53 Mg/m³Notched Izod Impact Strength , ISO 180, 23°C: 65 J/mCharpy Impact Strength, ASTM D256, 23°C, 4mm: 5.5 kJ/m²Volume Resistivity, ASTM D257: >1e15 ohm-cm

Injection	Nominal Value	Unit
Drying Temperature
--	100	°C
Pre-drying equipment	120 - 130	°C
Drying Time
--	1.0 - 2.0	hr
Pre-drying equipment	3.0	hr
Processing (Melt) Temp	230 - 260	°C
Mold Temperature	80.0 - 110	°C
Injection Rate	Moderate-Fast

Note Message
1 .	速率 A (50°C/h), 压力1 (10N)
2 .	速率 A (50°C/h), 载荷2 (50N)

Category:	PBT , Polybutylene Terephthalate
Manufacturer:	Taro Plast S.p.A.
Trademark:	TAROLOX
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	fOQs0v_TAROLOX-10-G4-DX03.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
VALOX™ HX3061HP resin	SABIC Innovative Plastics	PBT	VALOX™
Fiberfil® J-68/30/E/UV	Fiberfil® Engineered Plastics Inc.	PP Copolymer	Fiberfil®
FERREX® GPP20CC70HB BLUE	Ferro Corporation	PP Homopolymer	FERREX®
Flontech® FT-1-BLU2-FM-1	Guarniflon S.p.A. - Flontech Division	PTFE	Flontech®
Karina CLEAR PVC COMPOUND -E 80/200-SI-CRMT	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina