PELPRENE™ S9001
| Category: | TPEE , Thermoplastic Polyester Elastomer |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | PELPRENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fMXB1o_PELPRENE-S9001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PELPRENE™S9001 is a thermoplastic polyester elastomer (TPEE) product,. It is available in North America. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (2.00 mm) | 1.8 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 65% RH) | 0.28 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 78 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 49.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 400 | % | ASTM D638 |
| Flexural Modulus | 882 | MPa | ASTM D790 |
| Compressive Modulus | 39.2 | MPa | ASTM D695 |
| Taber Abrasion Resistance (1000 Cycles) | 6.00 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (50% Strain) | 44.1 | MPa | ASTM D412 |
| Tear Strength | 250 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 146 | °C | ASTM D648 |
| Brittleness Temperature | -50.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 207 | °C | ASTM D1525 |
| Melting Temperature | 223 | °C | DSC |
| CLTE - Flow | 1.4E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 7.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 30 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Hardness, JIS k6301, A scale: 9910% Compression Modulus, ASTM D695: 39.2 MPaCoefficient of Linear Thermal Expansion, TMA: 14e-5 1/K |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Axiall PVC 10850 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Karina WHITE PVC COMPOUND 802D10/ 1-E-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| MAJORIS ET360 - 8229 | AD majoris | PP, Unspecified | MAJORIS |
| Sylvin 9067-95LMW Grey 9368 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NORYL GTX™ GTX979 resin | SABIC Innovative Plastics Europe | PPE+PS+Nylon | NORYL GTX™ |