RTP 200.7 H
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fM1tzE_RTP-200-7-H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.90 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.90 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2830 | MPa | ASTM D638 |
| Tensile Strength | 62.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 7.5 | % | ASTM D638 |
| Flexural Modulus | 2480 | MPa | ASTM D790 |
| Flexural Strength | 86.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 210 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 800 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 304 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 232 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm, Values per RTP Company testing.) | HB | UL 94 |
| Additional Information |
|---|
| Molding Shrinkage, Linear-Flow, ASTM D955, 6.35mm: 13mm/m.Tensile Elongation, ASTM D638: 6-9%. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 274 - 288 | °C | |
| Middle Temperature | 274 - 288 | °C | |
| Front Temperature | 274 - 288 | °C | |
| Mold Temperature | 66.0 - 93.0 | °C | |
| Injection Pressure | 103 - 138 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOPAS® 9506F-500 | Polyplastics Co., Ltd. | COC | TOPAS® |
| UMG WOOD® W310AM | UMG ABS, Ltd. | ASA | UMG WOOD® |
| 4PROP® 9C22430 UV | 4Plas | PP Copolymer | 4PROP® |
| Kumho PS HFH 412 | Korea Kumho Petrochemical Co., Ltd. | PS (HIPS) | Kumho PS |
| PMC® 780 Dry/Wet | Smooth-On, Inc | PUR, Unspecified | PMC® |