Petra® 130 FR
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | BASF Corporation |
| Trademark: | Petra® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fLmV7C_Petra-130-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Petra 130 FR is a 30% glass fiber reinforced, flame retardant injection molding compound based on post-consumer and post-industrial recycle polyethylene terephthalate feedstocks. It is recognized as UL 94V-0/5VA by Underwriters Laboratories. It is also available in pigmented versions. Applications Petra 130 FR is generally recommended for applications such as electrical housing and bobbins. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.68 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 11100 | MPa | ISO 527-2 |
| Tensile Strength (Break, 23°C) | 130 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 2.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | ASTM D790 | ||
| -40°C | 12400 | MPa | |
| 23°C | 9700 | MPa | |
| 121°C | 2970 | MPa | |
| Flexural Strength | ASTM D790 | ||
| -40°C | 275 | MPa | |
| 23°C | 210 | MPa | |
| 121°C | 85.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 90 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 240 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 220 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 210 | °C | ISO 75-2/A |
| Peak Melting Temperature | 245 | °C | ASTM D3418, ISO 3146 |
| CLTE - Flow | 2.4E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | UL 746 | ||
| 0.300 mm | 75.0 | °C | |
| 0.750 mm | 155 | °C | |
| 1.50 mm | 155 | °C | |
| 3.00 mm | 155 | °C | |
| RTI Imp | UL 746 | ||
| 0.300 mm | 75.0 | °C | |
| 0.750 mm | 155 | °C | |
| 1.50 mm | 155 | °C | |
| 3.00 mm | 155 | °C | |
| RTI Str | UL 746 | ||
| 0.300 mm | 75.0 | °C | |
| 0.750 mm | 155 | °C | |
| 1.50 mm | 155 | °C | |
| 3.00 mm | 155 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | |||
| 1.50 mm | > 1.0E+13 | ohms·cm | ASTM D257 |
| -- | > 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 1.50 mm 1 | 22 | kV/mm | ASTM D149 |
| -- | 40 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | ||
| 100 Hz | 3.80 | ||
| 1 MHz | 3.60 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.020 | ||
| 1 MHz | 0.020 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.300 mm | V-0 | ||
| 0.750 mm | V-0 5VA | ||
| 1.50 mm | V-0 5VA | ||
| 3.00 mm | V-0 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 100 to 110 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCLAIR® 2710 | NOVA Chemicals | HDPE | SCLAIR® |
| VESTAMID® Care ML-GB30 | Evonik Industries AG | Nylon 12 | VESTAMID® Care |
| Fainplast PVC MPH 62 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Hipolyene X2 DP 4 | Zylog Plastalloys | TPO (POE) | Hipolyene |
| Hytrel® HTR8206 | DuPont Performance Polymers | TPC-ET | Hytrel® |