ACCUCOMP™ POL050L
| Category: | PC , Polycarbonate |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fLlMCH_ACCUCOMP-POL050L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUCOMP™ POL050L is a Polycarbonate (PC) product. It is available in North America. Primary characteristic: low viscosity. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1800 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 64.0 | MPa | |
| Break | 62.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 45 | % | |
| Break | 130 | % | |
| Flexural Modulus | 2800 | MPa | ASTM D790 |
| Flexural Strength | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 820 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 136 | °C | |
| 1.8 MPa, Unannealed | 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Baytec® U1281XA | Covestro - PUR | TSU | Baytec® |
| Clearflex® FG 106 | Versalis S.p.A. | LLDPE | Clearflex® |
| Ferro PP LPP20BN41HB | Ferro Corporation | PP, Unspecified | Ferro PP |
| Hifax BR 1149 A | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| Karina WHITE MINERAL CONC. MBU -E 10/0085-IE | Karina Ind. e Com. de Plásticos Ltda | EVA | Karina |