LNP™ LUBRICOMP™ KP002 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fLGKrp_LNPLUBRICOMPKP002compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP KP002 is a compound based on Acetal Copolymer resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound KL-4520 Product reorder name: KP002 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 2.2 | % | ASTM D955 |
| Transverse flow : 24 hours | 2.2 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 2.2 | % | ISO 294-4 |
| Flow direction : 24 hours | 2.2 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2760 | MPa | ASTM D638 |
| -- | 2330 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 46.9 | MPa | ASTM D638 |
| Yield 2 | 49.1 | MPa | ASTM D638 |
| Yield | 46.0 | MPa | ISO 527-2 |
| Yield | 49.6 | MPa | ISO 527-2/5 |
| Fracture | 46.9 | MPa | ASTM D638 |
| Fracture 3 | 48.1 | MPa | ASTM D638 |
| Fracture | 48.5 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield | 26 | % | ASTM D638 |
| Yield 4 | 18 | % | ASTM D638 |
| Yield | 29 | % | ISO 527-2 |
| Yield | 18 | % | ISO 527-2/5 |
| Fracture | 41 | % | ASTM D638 |
| Fracture 5 | 29 | % | ASTM D638 |
| Fracture | 28 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- | 2070 | MPa | ASTM D790 |
| 50.0mm span 6 | 1920 | MPa | ASTM D790 |
| -- | 2000 | MPa | ISO 178 |
| -- 7 | 1990 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| -- | 61.0 | MPa | ISO 178 |
| -- | 69.3 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.31 | ASTM D3702 Modified | |
| With Self-Static | 0.18 | ASTM D3702 Modified | |
| Flexural Strain at Break 8 | 7.0 | % | ISO 178 |
| Wear Factor - Washer | 8.50 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 9 | 5.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1100 | J/m | ASTM D4812 |
| 23°C 10 | 74 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 5.10 | J | ASTM D3763 |
| -- | 1.80 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 156 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 11 | 146 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 92.8 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 12 | 87.0 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.1E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 1.0E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 - 188 | °C | |
| Middle Temperature | 193 - 204 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Processing (Melt) Temp | 199 - 216 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 2 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEPAZ™ 235A | Mando Advanced Materials Co., Ltd. | PPA | SEPAZ™ |
| Sinkral® PD D 232/M4 | Versalis S.p.A. | ABS | Sinkral® |
| UBESTA 3030 XA | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| FM® 6604-1 | Cytec Industries Inc. | MAH-g | FM® |
| Polene LDPE J 4324 | TPI Polene Public Company Limited | LDPE | Polene LDPE |