NOVAPOL® TF-Y822 Series
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | NOVA Chemicals |
| Trademark: | NOVAPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fL1PlO_NOVAPOL-TF-Y822-Series.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TF-Y822-BP (750 ppm Slip, 3150 ppm Antiblock): Industrial packaging, high strength liners TF-Y822-CP (6000 ppm Antiblock): Heavy duty sacks, high strength packaging |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.921 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 25 µm, Blown Film | 230 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 280 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm, Blown Film | 12.0 | MPa | |
| TD : Yield, 25 µm, Blown Film | 12.0 | MPa | |
| MD : Break, 25 µm, Blown Film | 49.0 | MPa | |
| TD : Break, 25 µm, Blown Film | 42.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm, Blown Film | 560 | % | |
| TD : Break, 25 µm, Blown Film | 810 | % | |
| Dart Drop Impact (25 µm, Blown Film) | 130 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, Blown Film | 350 | g | |
| TD : 25 µm, Blown Film | 540 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 53 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 13 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Low Friction Puncture - Blown Film (25.0 µm) | 430 | J/cm | Internal Method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds PP-3235 | Ravago Manufacturing Americas, LLC | PP Copolymer | Ravago Compounds |
| Sup-tech T703 | Shanghai Suptech Engineering Plastics Co. Ltd. | PBT | Sup-tech |
| Toyolac® VX10-X01 | Toray Resin Company | ABS+PBT | Toyolac® |
| EMOPLEN® HP-R MTF 20 | EMAS Plastik San.Tic.AS. | PP Homopolymer | EMOPLEN® |
| Latigea B01 I6 | LATI S.p.A. | PLA | Latigea |