Latamid 66 B H-V0
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latamid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fKocA5_Latamid-66-B-H-V0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyamide 66 (PA 66). High fluidity. Heat stabilised. UL94 V-0 classified, halogens and red phosphorous free. Product UL certified. Blended with PA6. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.85 to 1.2 | % | |
| Flow : 2.00 mm | 0.80 to 1.1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 3800 | MPa | |
| 60°C | 1800 | MPa | |
| 90°C | 1100 | MPa | |
| 120°C | 800 | MPa | |
| 150°C | 600 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 80.0 | MPa | |
| Break, 23°C | 80.0 | MPa | |
| Break, 60°C | 55.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 4.0 | % | |
| Break, 23°C | 8.0 | % | |
| Break, 60°C | 50 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | 2.5 | kJ/m² | |
| -20°C | 2.8 | kJ/m² | |
| 23°C | 3.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 50 | kJ/m² | |
| 23°C | 55 | kJ/m² | |
| Notched Izod Impact | ASTM D256A | ||
| -40°C, 3.20 mm | 25 | J/m | |
| -20°C, 3.20 mm | 30 | J/m | |
| 23°C, 3.20 mm | 35 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 240 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 95.0 | °C | |
| Vicat Softening Temperature | 240 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 525 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 775 | °C | |
| 2.00 mm | 775 | °C | |
| Oxygen Index | 32 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 70.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP PP PPC4TF1.3-Natural | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| NILENE® P6 K25VA | Taro Plast S.p.A. | PP Homopolymer | NILENE® |
| Hifax EKC 244X grey | LyondellBasell Industries | TPO (POE) | Hifax |
| Kumho SBR 1507L | Korea Kumho Petrochemical Co., Ltd. | SBR, Emulsion | Kumho SBR |
| Therma-Tech™ TT9200-5003 EC Anthracite (EM10018998BJ) | PolyOne Corporation | PPS | Therma-Tech™ |