LNP™ FARADEX™ NS0031 compound
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ FARADEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fKRm7t_LNP-FARADEX-NS0031-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Faradex NS0031 is a compound based on PC+ABS blend resin containing non-brominated and non-chlorinated flame retardant system, Stainless Steel. Added features of this material include: EMI/RFI Shielding and ESD. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 12 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (265°C/10.0 kg) | 31.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.59 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.20 | % | |
| Equilibrium, 23°C, 50% RH | 0.10 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3120 | MPa | ASTM D638 |
| -- | 3010 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 61.0 | MPa | ASTM D638 |
| Yield | 59.5 | MPa | ISO 527-2/5 |
| Break 3 | 57.6 | MPa | ASTM D638 |
| Break | 55.2 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 3.4 | % | ASTM D638 |
| Yield | 3.2 | % | ISO 527-2/5 |
| Break 5 | 3.7 | % | ASTM D638 |
| Break | 4.4 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2970 | MPa | ASTM D790 |
| -- 7 | 3100 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 102 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 95.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 4.1 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 43 | J/m | ASTM D256 |
| 23°C | 55 | J/m | ASTM D256 |
| -30°C 10 | 5.7 | kJ/m² | ISO 180/1A |
| 23°C 11 | 5.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| -30°C | 590 | J/m | ASTM D4812 |
| 23°C | 690 | J/m | ASTM D4812 |
| -30°C 12 | 40 | kJ/m² | ISO 180/1U |
| 23°C 13 | 40 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 0.180 | J | ASTM D3763 |
| -- | 7.50 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 96.1 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 14 | 98.7 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 109 | °C | ASTM D1525, ISO 306/B50 11 15 |
| -- | 112 | °C | ISO 306/B120 |
| CLTE | |||
| Flow : -40 to 40°C | 5.7E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 5.5E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 6.6E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 6.4E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+5 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+7 | ohms·cm | ASTM D257 |
| Shielding Effectiveness (3.00 mm) | 47 | dB | Internal Method |
| Static Decay 16 | 10 | msec | FTMS 101B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Rear Temperature | 260 to 300 | °C | |
| Middle Temperature | 260 to 300 | °C | |
| Front Temperature | 265 to 300 | °C | |
| Nozzle Temperature | 265 to 300 | °C | |
| Processing (Melt) Temp | 270 to 300 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C | |
| Back Pressure | 4.00 | MPa | |
| Screw Speed | 30 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 mm |
| 15 . | Rate B (120°C/h), Loading 2 (50 N) |
| 16 . | 5000V to <50V |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® 90-E607B-75NT | Teknor Apex Company | EVA | Telcar® |
| Spartech Polycom PP5120F B2 | Spartech Polycom | PP, Unspecified | Spartech |
| DECAL® 5431 | Synres-Almoco BV | Phenolic | DECAL® |
| Plaslube® PA6/6 GF30 ML5 HS | Techmer Engineered Solutions | Nylon 66 | Plaslube® |
| StarFlex® 7060-1001 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarFlex® |