Elastollan® C90A
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | BASF Corp. Thermoplastic Polyurethanes |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fKPO3N_Elastollan-C90A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Elastollan® C90A exhibits excellent abrasion resistance and toughness, good hydrolytic stability, good heat, oil, fuel and solvent resistance. It has excellent damping characteristics and outstanding resistance to tear propagation. Elastollan® C90A is supplied uncolored in pellet form. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (210°C/21.6 kg) | 30 to 50 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 39.3 | MPa | ASTM D412 |
| Flexural Modulus (Injection Molded) | 48.3 | MPa | ASTM D790 |
| Taber Abrasion Resistance | 25.0 | mg | ASTM D1044 |
| Abrasion - DIN | 25 | mm³ | DIN 53516 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Softening Point - DMA | 113 | °C | Internal Method |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 10.3 | MPa | |
| 300% Strain | 22.8 | MPa | |
| Tensile Strength | 44.1 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 520 | % | ASTM D412 |
| Tear Strength 1 | 133 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 23°C, 22 hr | 25 | % | |
| 70°C, 22 hr | 40 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -38.0 | °C | Internal Method |
| Vicat Softening Temperature | 128 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Rear Temperature | 190 to 220 | °C | |
| Middle Temperature | 190 to 220 | °C | |
| Front Temperature | 190 to 220 | °C | |
| Nozzle Temperature | 210 to 225 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Cylinder Zone 1 Temp. | 170 to 210 | °C | |
| Cylinder Zone 3 Temp. | 170 to 210 | °C | |
| Cylinder Zone 5 Temp. | 170 to 210 | °C | |
| Adapter Temperature | 200 to 220 | °C | |
| Die Temperature | 195 to 215 | °C |
| Note Message | |
|---|---|
| 1 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 60G1 V25 NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| VENYL SW502H - 8229 | AD majoris | Nylon 6 | VENYL |
| apilon 52® TCLE 40 AF | API SpA | TPU-Polyether | apilon 52® |
| GELAST 5170A | Guang Sung Plastics (GSPL) | ABS | GELAST |
| Laticonther 52/11 CP1/600 F3 | LATI S.p.A. | PP Homopolymer | Laticonther |