Idealis 500
| Category: | HMWPE , High Molecular Weight Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Idealis |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fIhpUB_Idealis-500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: Braskem Idealis500 is the only High Molecular Weight Polyethylene resin in powder form specially designed for the compression molding process. Applications: Applications range from food handling cutting boards and playground toys to technical parts. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.951 | g/cm³ | ASTM D792 |
| Apparent Density | 0.45 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 0.70 | g/10 min | ASTM D1238 |
| Average Molecular Weight | 550000 | g/mol | Internal Method |
| Average Particle Size 1 | 170 | µm | ASTM D1921 |
| Intrinsic Viscosity | 4.7 | dl/g | ASTM D4020 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion 2 | 80 | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 63 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield | > 20.0 | MPa | |
| Break | > 30.0 | MPa | |
| Tensile Elongation (Break) | > 500 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 930 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | > 50 | kJ/m² | ISO 11542-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 80.0 | °C | ASTM D1525 4 |
| Peak Melting Temperature | 136 | °C | ASTM D3418 |
| Note Message | |
|---|---|
| 1 . | Dp50 |
| 2 . | Reference PE500 = 100, Sand Slurry Method |
| 3 . | Double-notched Specimen, 14° v-notch on both sides |
| 4 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Compoceran E103A | Arakawa Chemical Industries, Ltd. | Epoxy | Compoceran |
| ESENTTIA 60C90ND | Polipropileno del Caribe S.A. | PP Impact Copolymer | ESENTTIA |
| DuClear® QG 80 A | Ducor Petrochemicals BV | PP Random Copolymer | DuClear® |
| OTECH PVC OE9054 - Calendering | OTECH Corporation | PVC, Unspecified | OTECH PVC |
| Sylvin 8484-72 Natural | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |