LNP™ THERMOCOMP™ TF006 compound
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fIXYzG_LNP-THERMOCOMP-TF006-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP TF006 is a compound based on Polyurethane containing 30% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound TF-1006 Product reorder name: TF006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.10 to 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 0.50 to 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 0.40 | % | ISO 294-4 |
| Flow : 24 hr | 0.15 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.36 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.50 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1480 | MPa | ASTM D638 |
| -- | 1800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 50.0 | MPa | ASTM D638 |
| Yield | 51.0 | MPa | ISO 527-2/5 |
| Break 3 | 49.9 | MPa | ASTM D638 |
| Break | 51.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 16 | % | ASTM D638 |
| Yield | 16 | % | ISO 527-2/5 |
| Break 5 | 16 | % | ASTM D638 |
| Break | 16 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 1700 | MPa | ASTM D790 |
| -- 7 | 2190 | MPa | ISO 178 |
| Flexural Strength 8(Break, 50.0 mm Span) | 58.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 510 | J/m | ASTM D256 |
| 23°C 9 | 41 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | No Break | ASTM D4812 | |
| 23°C 10 | 130 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 19.5 | J | ASTM D3763 |
| -- | 17.6 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 167 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 167 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 78.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 85.0 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 2.7E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 2.8E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 1.3E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.0 to 104 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 193 to 210 | °C | |
| Middle Temperature | 193 to 216 | °C | |
| Front Temperature | 199 to 221 | °C | |
| Nozzle Temperature | 204 to 227 | °C | |
| Processing (Melt) Temp | 210 | °C | |
| Mold Temperature | 16.0 to 43.0 | °C | |
| Back Pressure | 0.170 to 0.340 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILVER® SA-3695 | Guangdong Silver Age Sci & Tech. Co., Ltd | TPE | SILVER® |
| THERMOLAST® K TC4GPN (Series: GP/FG) | KRAIBURG TPE | TPE | THERMOLAST® K |
| TUFNYL® SXXIC ZZ BEIGE | SRF Ltd. | Nylon 6 | TUFNYL® |
| Geon™ SF M7020 | PolyOne Corporation | PVC, Rigid | Geon™ SF |
| Sylvin 2946-80 Clear 8422 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |