AZDEL™ U421B02N (Transverse) Datasheet,PP Alloy,Azdel, Inc.-SHANGHAI SUSHENG

Message
Azdel® U421B02N is a uni-directional fiber and random glass mat reinforced polypropylene composite featuring excellent fiber distribution over long flow paths and complex part forms. This material allows highly directionalised reinforcement in applications where major loads are in defined planes. The material can be combined with Azdel random mat products to reinforce localized high stress paths, minimizing both part weight and costs.

General Information
Filler / Reinforcement	Glass fiber reinforced material, 42% filler by weight
Uses	Laminate
Forms	Sheet
Processing Method	Compression molding

Physical	Nominal Value	Unit	Test Method
Density	1.25	g/cm³	ISO 1183
Molding Shrinkage	0.40	%	ISO 294-4

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	4200	MPa	ISO 527-2
Tensile Stress (Yield)	50.0	MPa	ISO 527-2
Tensile Strain (Break)	2.0	%	ISO 527-2
Flexural Modulus	5000	MPa	ISO 178
Flexural Stress	130	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength	60	kJ/m²	ISO 179/2fnU
Multi-Axial Instrumented Impact Energy			ISO 6603-2
4.00, energy to power peak	58.0	J	ISO 6603-2
4.00, total impact penetration energy	100	J	ISO 6603-2
Multi-Axial Instrumented Impact Peak Force (4.00 mm)	13300	N	ISO 6603-2

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	145	°C	ISO 75-2/A
Melting Temperature (DSC)	166	°C	ISO 3146

Additional Information
Mass Per Unit Area, Azdel Test Method: 4.840 kg/m²Thickness, Azdel Test Method: 3.9 mmDensity, ISO 1183 Test Method: 1.21 g/cm³Density, ISO 1183 Test Method, Molded Plaque: 1.25 g/cm³Recrystallizing Temperature, ISO 3146 Test Method: 119 °CCTLE, Azdel Test Method, -30°C to 0°C, 3mm: 5.0e-5 1/°CCTLE, Azdel Test Method, 0°C to 120°C, 3mm: 3.3e-5 1/°CBlank Heat Parameters-Internal Temperature: 190 to 215°C-Surface Temperature: 205 to 220°C-Typical Heating Time for IR-System: 180 to 240°C-Typical Heating Time for Hot Air System: 240 to 480°CMould Temperature: 30 to 90°CMoulding Preasure: 150 to 250 barMinimum Pressing Speed: 20 mm/secTotal Cycle Time: 30 to 90 sec

Additional Information

Mass Per Unit Area, Azdel Test Method: 4.840 kg/m²Thickness, Azdel Test Method: 3.9 mmDensity, ISO 1183 Test Method: 1.21 g/cm³Density, ISO 1183 Test Method, Molded Plaque: 1.25 g/cm³Recrystallizing Temperature, ISO 3146 Test Method: 119 °CCTLE, Azdel Test Method, -30°C to 0°C, 3mm: 5.0e-5 1/°CCTLE, Azdel Test Method, 0°C to 120°C, 3mm: 3.3e-5 1/°CBlank Heat Parameters-Internal Temperature: 190 to 215°C-Surface Temperature: 205 to 220°C-Typical Heating Time for IR-System: 180 to 240°C-Typical Heating Time for Hot Air System: 240 to 480°CMould Temperature: 30 to 90°CMoulding Preasure: 150 to 250 barMinimum Pressing Speed: 20 mm/secTotal Cycle Time: 30 to 90 sec

Category:	PP Alloy , Polypropylene Alloy
Manufacturer:	Azdel, Inc.
Trademark:	AZDEL™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	fIOG6q_AZDEL-U421B02N-Transverse-.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Riblene® FF 39 D	Versalis S.p.A.	LDPE	Riblene®
POLYLAN T-120FW	POLYMA Kunststoff GmbH & Co. KG	ABS	POLYLAN
Tefzel® 750	DuPont Fluoropolymers	ETFE	Tefzel®
COSMOLEX® FS250A	TPC, The Polyolefin Company (Singapore) Pte Ltd	LLDPE	COSMOLEX®
Lupoy® 1201-08	LG Chem Ltd.	PC	Lupoy®