Type: Pearlbond™ ECO D900 is a linear, aromatic polyurethane, supplied in form of small white or lightly yellowish granules. Based on specialty polyol from renewable sources. Contains 75% of renewable materials as certified according to ASTM-D6866. Special features : High crystallization rate and a very high thermoplasticity level. It is used for Hot Melt adhesives. APLICATIONS Pearlbond™ ECO D900 is mainly used for textile coating for making shoe-stiffeners (toe puffs & counters), by extrusion or sintering process. Pearlbond™ ECO D900 can be used for making heat-sealable fabrics (thermobonding), obtained by coating processes such as scattering or dot-coating (powder or paste). In all cases, the product is previously ground into powder, by cryogenic grinding. The particle size of the powder will depend on the application technique to be used. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (170°C/2.16 kg) | 30 to 60 | g/10 min | ISO 1133 |
| Crystallinity | Extremely high | Internal Method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Renewable Content | 75 | % | ASTM D6866 |
| Softening Range | 70 to 75 | °C | Internal Method |
| Thermoplasticity | Very high | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 1 sec) | 52 | ISO 868 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 80.0 to 84.0 | °C | Internal Method |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity 1(160°C) | 930 | Pa·s | ISO 1133 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 40.0 to 50.0 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Cylinder Zone 1 Temp. | 90.0 | °C | |
| Cylinder Zone 2 Temp. | 100 to 120 | °C | |
| Cylinder Zone 3 Temp. | 100 to 120 | °C | |
| Cylinder Zone 4 Temp. | 100 to 120 | °C | |
| Die Temperature | 100 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 2.16 Kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD A 1005 | RTP Company | PBT | RTP |
| KOPELEN JH-370B | Lotte Chemical Corporation | PP Impact Copolymer | KOPELEN |
| Karina CLEAR PVC COMPOUND 57/200-D-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Polifor® L6 GF/20 NATURALE | SO.F.TER. SPA | PP Homopolymer | Polifor® |
| Moplen EP641P | PolyMirae | PP Impact Copolymer | Moplen |