LNP™ LUBRILOY™ U2000A compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRILOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fHI0do_LNP-LUBRILOY-U2000A-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRILOY U2000A is a compound based on Polyphthalamide resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRILOY* Compound U Product reorder name: U2000A |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 1.6 to 1.8 | % | ASTM D955 |
| Across Flow : 24 hr | 1.6 to 1.8 | % | ASTM D955 |
| Across Flow : 24 hr | 1.7 | % | ISO 294-4 |
| Flow : 24 hr | 1.7 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.30 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3450 | MPa | ASTM D638 |
| -- | 3530 | MPa | ISO 527-2/1 |
| Flexural Modulus | 2760 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.23 | ||
| vs. Itself - Static | 0.23 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 7.00 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 20.5 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 2 | 5.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 1300 | J/m | ASTM D4812 |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 4.80 | J | ASTM D3763 |
| -- | 16.3 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 164 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 3 | 183 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 106 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 103 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 7.1E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 7.1E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 304 to 316 | °C | |
| Middle Temperature | 304 to 316 | °C | |
| Front Temperature | 304 to 316 | °C | |
| Processing (Melt) Temp | 310 to 316 | °C | |
| Mold Temperature | 121 to 149 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VESTAMID® NRG 1001 natural color | Evonik Industries AG | Nylon 12 | VESTAMID® NRG |
| WPP PP PPH3GF3-UV Black | Washington Penn Plastic Co. Inc. | PP, Unspecified | WPP PP |
| Bayblend® M301 FR | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| Hostacom X M3 T08 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Laprene® 830000844 | SO.F.TER. SPA | SEBS | Laprene® |