CoolPoly® E1201
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Celanese Corporation |
| Trademark: | CoolPoly® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fGudt5_CoolPoly-E1201.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CoolPoly E series of thermally conductive plastics transfers heat, a characteristic previously unavailable in injection molding grade polymers. CoolPoly is lightweight, netshape moldable and allows design freedom in applications previously restricted to metals. The E series is electrically conductive and provides inherent EMI/RFI shielding charactersitics. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.35 | % | ASTM D955 |
| Transverse flow | 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5620 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 22.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 1.0 | % | ISO 527-2 |
| Flexural Modulus | 5410 | MPa | ISO 178 |
| Flexural Stress | 37.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.3 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 5.4 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Heat | 1280 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 10 | W/m/K | ASTM C177 |
| Additional Information |
|---|
| The value listed as Thermal Conductivity, ASTM C177, was tested in accordance with ASTM E1461.The value listed as Mold Shrinkage, ASTM D955, was tested in accordance with ASTM D551.The value listed as Specific Heat ASTM C351, was teste in accordance with ASTM E1461.Thermal Diffusivity, ASTM E1461: 0.0587 cm²/sec |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Dew Point | -20.0 | °C | |
| Rear Temperature | 190 - 220 | °C | |
| Middle Temperature | 210 - 230 | °C | |
| Front Temperature | 215 - 245 | °C | |
| Processing (Melt) Temp | 215 - 245 | °C | |
| Mold Temperature | 20.0 - 65.0 | °C | |
| Injection Pressure | 35.0 - 105 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 20.0 - 55.0 | MPa | |
| Back Pressure | 0.00 - 0.350 | MPa | |
| Screw Speed | 20 - 60 | rpm | |
| Screw Compression Ratio | 2.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP2409 | LyondellBasell Industries | PP Homopolymer | Moplen |
| THERMORUN® QT99ZA | Mitsubishi Chemical Corporation | TPO (POE) | THERMORUN® |
| VAMPTER C 0023 V0 | Vamp Tech | PC+PBT | VAMPTER |
| ASI POLYPROPYLENE 3515 | A. Schulman Inc. | PP Copolymer | ASI POLYPROPYLENE |
| Clariant Nylon 6/6 66G25-L | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |