UNIBRITE® UB-401
| Category: | AES , Acrylonitrile Ethylene Styrene |
| Manufacturer: | Nippon A&L Inc. |
| Trademark: | UNIBRITE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fEdsaG_UNIBRITE-UB-401.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UNIBRITE® UB-401 is an Acrylonitrile Ethylene Styrene (AES) material. It is available in Asia Pacific or North America for extrusion. Primary attribute of UNIBRITE® UB-401: Flame Rated. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.04 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.60 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 104 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 51.0 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 2350 | MPa | ISO 178 |
| Flexural Stress (23°C) | 74.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 30 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 84.0 | °C | ISO 75-2/A |
| CLTE - Flow (23 to 80°C) | 8.5E-5 | cm/cm/°C | JIS K7197 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | > 3.0 | hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vydyne® R530H Black | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| CGPC PVC R-10X NI Bottle Blowing | China General Plastics Corporation | PVC, Flexible | CGPC PVC |
| Complet® LGF20-PA66 | PlastiComp, Inc. | Nylon 66 | Complet® |
| Geon™ BIO HC5155 | PolyOne Corporation | PVC, Flexible | Geon™ BIO |
| EPAMOULD 660D30 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |