OMIKRON BE 937 NAT
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | TECNOPOL |
| Trademark: | OMIKRON |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fEXZsg_OMIKRON-BE-937-NAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
OMIKRON BE 937 is an homopolymer polypropylene reinforced with 40% of glass fibre for injection moulding, high processability. Excellent performances in thermal and detergent resistance. It is available in natural. Coloured on demand. OMIKRON BE 937 is suitable for moulding of items requiring stiffness and dimensional stability . |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 98.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 7500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 13 | kJ/m² | ISO 180 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Aging (150°C) | > 2.7 | month | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 148 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 137 | °C | ISO 306/B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 230 - 260 | °C | |
| Middle Temperature | 230 - 260 | °C | |
| Front Temperature | 230 - 260 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Injection Pressure | 90.0 - 110 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 5.00 - 10.0 | MPa |
| Injection instructions |
|---|
| Post Pressure: 60 to 80 bar |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® C 218 V30 BLACK | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| Vydyne® R525H BK0201 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Geon™ Vinyl Flexible R356AE | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Axiall PVC 8245 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| PENTALLOY BS 6 GV30 H natural | PENTAC Polymer GmbH | ABS+Nylon | PENTALLOY BS |