Piolen® P T20A19
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | PiO Kunststoffe GmbH & Co KG |
| Trademark: | Piolen® P |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fEKDib_Piolen-P-T20A19.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Piolen® P T20A19 is a Polypropylene Homopolymer (PP Homopolymer) product filled with 20% talc. It can be processed by injection molding and is available in Europe. Applications of Piolen® P T20A19 include automotive, cleaning applications and coating applications. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 19 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 32.0 | MPa | |
| Break | 30.3 | MPa | |
| Tensile Strain (Break) | 6.3 | % | ISO 527-2 |
| Flexural Modulus | 2200 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 156 | °C | ISO 306/A |
| -- | 96.0 | °C | ISO 306/B |
| Peak Crystallization Temperature (DSC) | 164 to 167 | °C | ISO 3146 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| YUPLENE® R366Y | SK Global Chemical | PP Random Copolymer | YUPLENE® |
| DISTRUMID 66GF30HS | Distrupol | Nylon 66 | DISTRUMID |
| Elastron® G G400.A80.B | Elastron USA, Inc. | SEBS | Elastron® G |
| Sylvin 8999-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LEXAN™ EXL9132 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |