InnoPlus HD1100J
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | PTT Global Chemical Public Company Limited |
| Trademark: | InnoPlus |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fDy7bn_InnoPlus-HD1100J.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
InnoPlus HD1100J and HD1600J are high density polyethylene injection molding grade. They are tailored with narrow molecular weight distribution (MWD) and high flow ability. They have optimum strength property which used for general part, auto part, toy and house ware. Typical Application: Toys, Auto parts, Household products |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.958 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
| ESCR - condition B, 25% Igepal, F50 | Initial Break | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 64 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 29.4 | MPa | |
| Break | 22.6 | MPa | |
| Tensile Elongation (Break) | 60 | % | ASTM D638 |
| Apparent Bending Modulus | 981 | MPa | ASTM D747 |
| Flexural Modulus | 1230 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 1 | 39 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 116 | °C | ASTM D1525 2 |
| Peak Melting Temperature | 128 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 165 to 190 | °C | |
| Middle Temperature | 165 to 190 | °C | |
| Front Temperature | 165 to 190 | °C | |
| Nozzle Temperature | 180 to 195 | °C |
| Note Message | |
|---|---|
| 1 . | Complete break |
| 2 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4003.3 | RTP Company | PPA | RTP |
| ULTEM™ 2212R resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| HiFill® PEEK CF40 HF | Techmer Engineered Solutions | PEEK | HiFill® |
| Karina WHITE PVC COMPOUND 800-10/177-Y-ERYB-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| NORYL™ FE1630PW resin | SABIC Innovative Plastics Europe | PPE+PS | NORYL™ |