SAXALEN™ PPH303G20
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | SAX Polymers |
| Trademark: | SAXALEN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fCXtEV_SAXALEN-PPH303G20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SAXALEN PPH303G20 is a 20% glass filled Polypropylene - Homopolymer injection moulding grade with good stiffness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 11.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4400 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 59.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 3900 | MPa | ISO 178 |
| Flexural Stress 2 | 94.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 33 | kJ/m² | |
| 23°C | 42 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 30 | kJ/m² | |
| 23°C | 34 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 60.0 mm Span) | 136 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 130 | °C | ISO 306/B120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytron® P30N07 | Polyram Ram-On Industries | PP Homopolymer | Polytron® |
| Premier PR350M | Premier Polymers, LLC. | PP Random Copolymer | Premier |
| SEPAZ™ LB30 | Mando Advanced Materials Co., Ltd. | Nylon 6 | SEPAZ™ |
| TPUCO® TPUE-E95 | Taiwan PU Corporation | TPU-Polyester | TPUCO® |
| Elastron® D D400.A50.T | Elastron USA, Inc. | SBS | Elastron® D |