Alathon® M6138
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Alathon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fCUCVY_Alathon-M6138.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ALATHON M6138 is high density polyethylene resin for use in injection molding applications. This resin exhibits good impact resistance and high stiffness. Typical applications include agricultural bins, crates, open head pails, trays and consumer durable goods. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.961 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.53 to 0.59 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.8 | g/10 min | ASTM D1238 |
| Spiral Flow | 20.3 | cm | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 72 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | ASTM D638 | ||
| -- | 1220 | MPa | |
| 1% Secant | 939 | MPa | |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 31.9 | MPa | |
| Break | 21.7 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 7.0 | % | |
| Break | 810 | % | |
| Flexural Modulus 4 | ASTM D790 | ||
| -- | 1740 | MPa | |
| 1% Secant | 1640 | MPa | |
| 2% Secant | 1370 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 60 | J/m | ASTM D256 |
| Unnotched Izod Impact (-18°C) | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 81.7 | °C | ASTM D648 |
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 131 | °C | ASTM D1525 |
| Peak Melting Temperature | 134 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 118 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 232 | °C | |
| Middle Temperature | 243 | °C | |
| Front Temperature | 246 | °C | |
| Nozzle Temperature | 246 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| 3 . | Type IV, 50 mm/min |
| 4 . | 13 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6600 GV 20 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| VAMPAMID 6 3025 V0 DF | Vamp Tech | Nylon 6 | VAMPAMID |
| LUVOCOM® 1105-8059 VP | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| MAJ'ECO DP374SAR | AD majoris | PP, Unspecified | MAJ'ECO |
| VALOX™ SHF4960 resin | SABIC Innovative Plastics Europe | PBT | VALOX™ |