Dow Corning® C6-350LH

Category:	Silicone , Silicone
Manufacturer:	Dow Corning Corporation
Trademark:	Dow Corning®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	fCDS5q_DowCorningC6350LH.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
High Consistency Rubber with platinum cure Raw materials with enhanced physical properties for healthcare industry fabrication APPLICATIONS DOW Corning Class VI Elastomer C6-350LH is a platinum-catalyzed heat-cured silicone High Consistency Rubber for part fabrication, extrusion and medical devices, including those intended for implantation in humans for up to 29 days. This material exhibits enhanced physical properties and may be particularly beneficial for fabricating devices and products where high resilience (low hysteresis loss) is important. DESCRIPTION DOW CORNING C6-350LH Elastomer, Parts A & B is a two-part platinum-catalyzed silicone elastomer. It is supplied as a two-part kit (Part A & B), equal portions of which must be thoroughly blended together prior to use. The elastomer is thermally cured via an addition-cure (platinum-catalyzed) reaction. When blended and cured as indicated, the resulting elastomer consists of crosslinked dimethyl and methyl-vinyl siloxane copolymers and reinforcing silica. DOW CORNING C6-350LH Elastomer differs from our conventional high consistency rubber (HCR) products in that it exhibits enhanced physical properties. In particular, it exhibits lower hysteresis losses (more resiliency) compared to other platinum-catalyzed HCRs, and a reduction in crack growth propagation. The elastomer can normally be used without any post-cure, although if necessary, this may be employed to stabilize final properties. Furthermore, the elastomer is heat stable up to 204°C (399°F), can be autoclaved, and exhibits high gas permeability compared with most thermoset elastomers and thermoplastics.

Message

High Consistency Rubber with platinum cure Raw materials with enhanced physical properties for healthcare industry fabrication

APPLICATIONS
DOW Corning Class VI Elastomer C6-350LH is a platinum-catalyzed heat-cured silicone High Consistency Rubber for part fabrication, extrusion and medical devices, including those intended for implantation in humans for up to 29 days.

This material exhibits enhanced physical properties and may be particularly beneficial for fabricating devices and products where high resilience (low hysteresis loss) is important.

DESCRIPTION
DOW CORNING C6-350LH Elastomer, Parts A & B is a two-part platinum-catalyzed silicone elastomer. It is supplied as a two-part kit (Part A & B), equal portions of which must be thoroughly blended together prior to use. The elastomer is thermally cured via an addition-cure (platinum-catalyzed) reaction. When blended and cured as indicated, the resulting elastomer consists of crosslinked dimethyl and methyl-vinyl siloxane copolymers and reinforcing silica.

DOW CORNING C6-350LH Elastomer differs from our conventional high consistency rubber (HCR) products in that it exhibits enhanced physical properties. In particular, it exhibits lower hysteresis losses (more resiliency) compared to other platinum-catalyzed HCRs, and a reduction in crack growth propagation.

The elastomer can normally be used without any post-cure, although if necessary, this may be employed to stabilize final properties. Furthermore, the elastomer is heat stable up to 204°C (399°F), can be autoclaved, and exhibits high gas permeability compared with most thermoset elastomers and thermoplastics.

General Information
Features	High Gas Permeability No frost Good coloring High pressure heating resistance Elastic
Uses	Medical/nursing supplies
Agency Ratings	ISO 10993-Part I USP Class VI

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.15	g/cm³	ASTM D792
Molding Shrinkage - Flow	1.7	%

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	49		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress (200% Strain)	2.21	MPa	ASTM D412
Tensile Strength	8.84	MPa	ASTM D412
Tensile Elongation (Break)	730	%	ASTM D412
Tear Strength ¹	37.8	kN/m	ASTM D624
Compression Set	60	%	ASTM D395

Note Message
1 .	B mould

Resin Grade	Manufacturer	Category	Trademark
SAXALEN™ PPH319FX21	SAX Polymers	PP Homopolymer	SAXALEN™
NOVADURAN® 5817GN2-30	Mitsubishi Engineering-Plastics Corp	PBT Alloy	NOVADURAN®
Delta PCA 1103	Delta Polymers	PC+ABS	Delta
DIOSHY® LP-880	DIOSHY Co.,Ltd.	SEBS+SBS	DIOSHY®
Mediprene® 520450M	ELASTO	SEBS	Mediprene®