Sindustris POM HI516W
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris POM |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fC8T06_Sindustris-POM-HI516W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris POM HI516W is an Acetal (POM) Homopolymer material. It is available in Asia Pacific for injection molding. Important attributes of Sindustris POM HI516W are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 1.7 to 2.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 64 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 41.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 67 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 1420 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 47.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.40 mm) | 73 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 79.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 150 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 110 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 160 to 180 | °C | |
| Middle Temperature | 170 to 190 | °C | |
| Front Temperature | 180 to 200 | °C | |
| Nozzle Temperature | 180 to 200 | °C | |
| Processing (Melt) Temp | 200 to 220 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Back Pressure | 0.490 to 3.04 | MPa | |
| Screw Speed | 80 to 110 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polymer-E B231 | Asia Polymer Corporation (APC) | LDPE | Polymer-E |
| RheTech Thermoplastic Polyolefin FT4200-01 | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| VITAMIDE® BB16BK6671 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| TOTAL Polypropylene PPR 6232 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| apigo® 8376 BS/65 | API SpA | TPO (POE) | apigo® |