LNP™ STAT-KON™ AE004 compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fBKUZF_LNP-STAT-KON-AE004-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* AE004 is a compound based on ABS resin containing 20% Carbon Fiber. Added feature of this material is: Electrically Conductive. Also known as: LNP* STAT-KON* Compound AC-1004 Product reorder name: AE004 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.10 - 0.30 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.30 - 0.60 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.25 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.25 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 13000 | MPa | ASTM D638 |
| Tensile Strength | |||
| Fracture 2 | 95.0 | MPa | ASTM D638 |
| Fracture | 90.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 3 | 2.6 | % | ASTM D638 |
| Fracture | 2.3 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 4 | 10600 | MPa | ASTM D790 |
| -- 5 | 12800 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 152 | MPa | ISO 178 |
| Fracture, 50.0mm span 6 | 131 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 64 | J/m | ASTM D256 |
| 23°C 7 | 6.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 320 | J/m | ASTM D4812 |
| 23°C 8 | 16 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 64.0mm span 9 | 105 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 213 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 10 | 101 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow : -30 to 30°C | 2.0E-5 | cm/cm/°C | ASTM D696 |
| Lateral : -30 to 30°C | 7.2E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+4 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 - 0.10 | % | |
| Rear Temperature | 204 - 216 | °C | |
| Middle Temperature | 232 - 243 | °C | |
| Front Temperature | 266 - 277 | °C | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 71.1 - 82.2 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ PPH-30T Nat | PolyOne Corporation | PP Homopolymer | Maxxam™ |
| Sumikon® FM-TK200 | Sumitomo Bakelite Co., Ltd. | PPS | Sumikon® |
| AIE PC 1010F-T6 | Asia International Enterprise (Hong Kong) Limited | PC | AIE PC |
| Aristech Quarite Plus® | Aristech Acrylics LLC | Acrylic, Unspecified | Aristech |
| Grilamid® XE 4071 black 9992 | EMS-GRIVORY | Nylon 612 | Grilamid® |