Promyde® B30 P2 G40 MI
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | NUREL, S.A. |
| Trademark: | Promyde® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fBEpFf_Promyde-B30-P2-G40-MI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Promyde B30 P2 G40 MI is a Polyamide 6 injection moulding grade with 40% glass fibre, impact modified and heat stabilized. CHARACTERISTICS This material is distinguished by high mechanical strength and impact resistance. Parts made from Promyde B30 P2 G40 MI have particularly high dimensional stability and creep strength. APPLICATIONS Promyde B30 P2 G40 MI is used in a wide range of applications where a combination of mechanical properties, thermal resistance and resistance to breakage by impact is needed. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.43 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 30.0 | -- | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 4.9 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.5 | -- | % | ISO 62 |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 11000 | 6200 | MPa | ISO 527-2/1 |
| Tensile Stress (23°C) | 170 | 115 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 4.5 | 9.5 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 9500 | 6000 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 240 | 140 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 17 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 22 | 40 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 95 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 100 | 130 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 205 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 3 | 222 | -- | °C | ISO 3146 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 80°C | 1.5E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 5.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 4.00 | 5.50 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.023 | 0.20 | IEC 60250 | |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.50 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Back Pressure: moderate |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarflen® DN-R | Grupa Azoty S.A. | PTFE | Tarflen® |
| ALTECH® PA6 C 1000/586 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| Cevian®-V 910B (Type T) | Daicel Polymer Ltd. | ABS | Cevian®-V |
| Generic Nylon 6 - Talc | Generic | Nylon 6 | Generic |
| Hylac® GP74G20 | Ravago Manufacturing Americas, LLC | ABS | Hylac® |