INSULCAST® 125/INSULCURE 11B
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | ITW Polymers Coatings North America |
| Trademark: | INSULCAST® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fBBVwe_INSULCAST-125-INSULCURE-11B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| INSULCAST 125 is a low viscosity, general purpose potting and casting compound. The low viscosity enables it to be used in potting densely packed modules, thereby insuring good flow and penetration around components. INSULCAST 125 contains non-abrasive fillers and is suitable for automatic dispensing equipment. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore D) | 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 79.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Strength | 103 | MPa | ASTM D790 |
| Compressive Strength | 89.6 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE - Flow | 4.8E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.62 | W/m/K | |
| Heat Deflection Temperature | 155 | °C | |
| Service Temperature | 155 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 9.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 4.20 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 0.020 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 9.0 to 10 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Shelf Life (25°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 1 | Amber | ||
| -- 2 | Black | ||
| Density | ASTM D1475 | ||
| -- 3 | 0.948 | g/cm³ | |
| -- 4 | 1.55 | g/cm³ | |
| Viscosity | |||
| -- 5 | 0.70 | Pa·s | |
| 25°C 6 | 2.5 | Pa·s | |
| -- 7 | 7.5 | Pa·s | |
| Curing Time 8 | 3.0 | hr | |
| Pot Life 9(25°C) | 150 | min |
| Note Message | |
|---|---|
| 1 . | INSULCURE 11B |
| 2 . | INSULCAST 125 |
| 3 . | INSULCURE 11B |
| 4 . | INSULCAST 125 |
| 5 . | INSULCURE 11B |
| 6 . | Mixed |
| 7 . | INSULCAST 125 |
| 8 . | 2 hours at 80°C plus 1 hour at 150°C |
| 9 . | 100 gram mass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® STAMAX 40YM243 resin | SABIC Innovative Plastics | PP, Unspecified | SABIC® STAMAX |
| SCHULAMID® 66 GF 30 GID | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| Next Nylon 66 Prime Series PGHS33-01BK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| LTP PA6125 | Chengdu Letian Plastics Co., Ltd | TP, Unspecified | LTP |
| Sylvin 9604-80 CLEAR 896 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |