Petrotene® PP A3 G40 NTLA010 PH306
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Petrotene® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fB8GGs_Petrotene-PP-A3-G40-NTLA010-PH306.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Natural polypropylene with 40% fiberglass, ideal for injection molding, resistant to oil, grease and many solvents, has a high tensile strength and higher HDT, and excellent dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 7.0 to 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 90.0 | MPa | ISO 527-2 |
| Flexural Modulus | 6900 | MPa | ISO 178 |
| Flexural Stress | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 130 | °C | |
| 1.8 MPa, Unannealed | 155 | °C | |
| Vicat Softening Temperature | 140 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 40 | kV/mm | ASTM D149 |
| Dissipation Factor (1 kHz) | 1.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® 1021GF6 BLACK 0179 | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |
| MonoSol® AF L330 | MonoSol, LLC | PVOH | MonoSol® |
| Axiall PVC 8700 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| LNP™ LUBRICOMP™ DFL32P compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |
| PLEXIGLAS® Sheet Resist 100 | Evonik Industries AG | Acrylic (PMMA) | PLEXIGLAS® Sheet |