LNP™ THERMOCOMP™ AF006XXZ compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fArHNL_LNP-THERMOCOMP-AF006XXZ-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP AF006XXZ is a compound based on ABS resin containing 30% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound AF-1006 Product reorder name: AF006XXZ |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.20 | % | |
| Across Flow : 24 hr | 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Break | 96.5 | MPa | ASTM D638 |
| Break | 83.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 1.8 | % | ASTM D638 |
| Break | 1.7 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 9170 | MPa | ASTM D790 |
| -- | 8000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 153 | MPa | ASTM D790 |
| -- | 119 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 1 | 5.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 280 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 102 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 2 | 102 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Rear Temperature | 204 to 216 | °C | |
| Middle Temperature | 232 to 243 | °C | |
| Front Temperature | 266 to 277 | °C | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 71.1 to 82.2 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TechnoFin GF 40 | TechnoCompound GmbH | PP, Unspecified | TechnoFin |
| MonoSol® M8630 - 2 mil | MonoSol, LLC | PVOH | MonoSol® |
| LNP™ KONDUIT™ PX11313 compound | SABIC Innovative Plastics Asia Pacific | Nylon 6 | LNP™ KONDUIT™ |
| OxyVinyls® 225 | OxyVinyls, LP | PVC Homopolymer | OxyVinyls® |
| Polimid B AV HF | Poliblend S.p.a. | Nylon 6 | Polimid B |