VENYL SG200
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fAHkGz_VENYL-SG200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL SG200 is a 20 % glass fibre reinforced polyamide 6 intended for Injection moulding. APPLICATIONS VENYL SG200 has been developed especially for very demanding applications in automotive industry and electrical parts. Products requiring excellent combination between thermal and mechanical properties. VENYL SG200 is available in both natural (VENYL SG200) and black (VENYL SG200-8229) but other colours can be provided on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.27 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.40 to 0.80 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.6 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (L-Scale) | 102 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 6500 | 4500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 115 | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.5 | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 5500 | 3300 | MPa | ISO 178 |
| Flexural Stress | 200 | 120 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 8.0 | 12 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 30 | 40 | kJ/m² | ISO 179 |
| Notched Izod Impact | 60 | 75 | J/m | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 200 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 190 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | DIN 53482 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | DIN 53482 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Rear Temperature | 245 to 265 | °C | |
| Middle Temperature | 250 to 270 | °C | |
| Front Temperature | 255 to 275 | °C | |
| Nozzle Temperature | 255 to 275 | °C | |
| Mold Temperature | 85.0 to 110 | °C | |
| Injection Pressure | 85.0 to 110 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Chiao Fu PP PP212GM40 NAT | Chiao Fu Enterprises Co., Ltd. | PP, Unspecified | Chiao Fu PP |
| Interpol 47-5117/47-5205 | Cook Composites and Polymers | PUR-Ester | Interpol |
| Karina IVORY PVC COMPOUND -E 807D35/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lupox® LW5303 | LG Chem Ltd. | PBT | Lupox® |
| Plastiglas Novanite® (Granite) | Plastiglas de Mexico S.A de C.V. | Acrylic, Unspecified | Plastiglas |